| Titre : |
Mechanical properties of PVC well screen and casing. |
| Type de document : |
texte imprimé |
| Auteurs : |
Swihart, J. |
| Mention d'édition : |
U.S. Department of the interior |
| Editeur : |
U.S. Department of the Interior |
| Année de publication : |
1989 |
| ISBN/ISSN/EAN : |
CI-06872 |
| Note générale : |
Tensiles, collapse, and stiffness tests were run on two manufacturers shcedule 80 and class 200,8 - and 12 -inch - diameter specimens of PVC (polyvinyl chloride) well casing / well sreen / Flush-fit threaded koints / and flush - fit, solvent-welded, splip-fit joints. Watertightness tests were also run on the flush-fit threaded joints. The solvent-welded, splip-fit tensile specimens were cured in bath air and water at temperatures ranging from 32°F to 100°F, with cure times before testing ranging from 2 minutes to 21 days... |
| Langues : |
Anglais (eng) |
| Mots-clés : |
PUITS Forage Equipement Hydraulique Limite d'élasticité Propriété mécanique Effondrement |
| Index. décimale : |
621.2 Hydraulique : turbines, pompes, accumulateurs, transmission hydraulique |
| Résumé : |
Tensiles, collapse, and stiffness tests were run on two manufacturers shcedule 80 and class 200,8 - and 12 -inch - diameter specimens of PVC (polyvinyl chloride) well casing / well sreen / Flush-fit threaded koints / and flush - fit, solvent-welded, splip-fit joints. Watertightness tests were also run on the flush-fit threaded joints. The solvent-welded, splip-fit tensile specimens were cured in bath air and water at temperatures ranging from 32°F to 100°F, with cure times before testing ranging from 2 minutes to 21 days... |
| Note de contenu : |
Tensiles, collapse, and stiffness tests were run on two manufacturers shcedule 80 and class 200,8 - and 12 -inch - diameter specimens of PVC (polyvinyl chloride) well casing / well sreen / Flush-fit threaded koints / and flush - fit, solvent-welded, splip-fit joints. Watertightness tests were also run on the flush-fit threaded joints. The solvent-welded, splip-fit tensile specimens were cured in bath air and water at temperatures ranging from 32°F to 100°F, with cure times before testing ranging from 2 minutes to 21 days... |
Mechanical properties of PVC well screen and casing. [texte imprimé] / Swihart, J. . - U.S. Department of the interior . - U.S. Department of the Interior, 1989. ISSN : CI-06872 Tensiles, collapse, and stiffness tests were run on two manufacturers shcedule 80 and class 200,8 - and 12 -inch - diameter specimens of PVC (polyvinyl chloride) well casing / well sreen / Flush-fit threaded koints / and flush - fit, solvent-welded, splip-fit joints. Watertightness tests were also run on the flush-fit threaded joints. The solvent-welded, splip-fit tensile specimens were cured in bath air and water at temperatures ranging from 32°F to 100°F, with cure times before testing ranging from 2 minutes to 21 days... Langues : Anglais ( eng)
| Mots-clés : |
PUITS Forage Equipement Hydraulique Limite d'élasticité Propriété mécanique Effondrement |
| Index. décimale : |
621.2 Hydraulique : turbines, pompes, accumulateurs, transmission hydraulique |
| Résumé : |
Tensiles, collapse, and stiffness tests were run on two manufacturers shcedule 80 and class 200,8 - and 12 -inch - diameter specimens of PVC (polyvinyl chloride) well casing / well sreen / Flush-fit threaded koints / and flush - fit, solvent-welded, splip-fit joints. Watertightness tests were also run on the flush-fit threaded joints. The solvent-welded, splip-fit tensile specimens were cured in bath air and water at temperatures ranging from 32°F to 100°F, with cure times before testing ranging from 2 minutes to 21 days... |
| Note de contenu : |
Tensiles, collapse, and stiffness tests were run on two manufacturers shcedule 80 and class 200,8 - and 12 -inch - diameter specimens of PVC (polyvinyl chloride) well casing / well sreen / Flush-fit threaded koints / and flush - fit, solvent-welded, splip-fit joints. Watertightness tests were also run on the flush-fit threaded joints. The solvent-welded, splip-fit tensile specimens were cured in bath air and water at temperatures ranging from 32°F to 100°F, with cure times before testing ranging from 2 minutes to 21 days... |
|  |